Abstract

Metal–organic frameworks (MOFs) are being intensively explored as filler materials for polymeric membranes primarily due to their high polymer affinity, large pore volumes, and alterable pore functionalities, but the development of MOF-based ultrafiltration (UF) membranes for water treatment lags behind. Herein, poly(sulfobetaine methacrylate) (PSBMA)-functionalized MOF UiO-66-PSBMA was developed, and incorporated into polysulfone (PSf) casting solution to fabricate novel hybrid UF membranes via phase-inversion method. The resultant UiO-66-PSBMA/PSf membrane exhibited significantly improved water flux (up to 602 L m–2 h–1), which was 2.5 times that of the pristine PSf membrane (240 L m–2 h–1) and 2 times that of UiO-66-NH2/PSf membrane (294 L m–2 h–1), whereas the rejection of UiO-66-PSBMA/PSf membrane was still maintained at a high level. Moreover, UiO-66-PSBMA/PSf membrane exhibited improved antifouling performance. The improvement of membrane performances could be attributed to the well-tailored properties of UiO-66-PSBMA. On one hand, the excellent dispersion and compatibility of UiO-66-PSBMA ensured the formation of a uniform structure with few defects. On the other hand, the superhydrophilicity of UiO-66-PSBMA could accelerate the exchange rate between solvent and nonsolvent, resulting in a more hydrophilic surface and a more porous structure. Besides, UiO-66-PSBMA nanoparticles in the thin layer provided additional flow paths for water permeation through their hydrophilic porous structure as well as the tiny interspace between PSf matrix. This study indicates the great application potential of UiO-66-PSBMA in fabricating hybrid UF membranes and provides a useful guideline to integrate other modified hydrophilic MOFs to design UF membranes for water treatment.

<<全文链接>>